Mechanical behaviour and durability assessment of Fibre Reinforced Cementitious Matrix (FRCM) strengthening systems.

In recent years, the seismic vulnerability of existing masonry buildings has been underscored by the destructive impacts of earthquakes. Therefore, Fibre Reinforced Cementitious Matrix (FRCM) retrofitting systems have gained prominence due to their high strength-to-weight ratio, compatibility with substrates, and potential reversibility. However, concerns linger regarding the durability of these systems when subjected to long-term environmental conditions. This doctoral dissertation addressed these concerns by studying the effects of mild temperature variations on three FRCM systems, featuring basalt, glass, and aramid fibre textiles with lime-based mortar matrices. The study subjected various specimens, including mortar triplets, bare textile specimens, FRCM coupons, and single-lap direct shear wallets, to thermal exposure. A novel approach utilizing embedded thermocouple sensors facilitated efficient monitoring and active control of the conditioning process. A shift in the failure modes was obtained in the single lap-direct shear tests, alongside a significant impact on tensile capacity for both textiles and FRCM coupons. Subsequently, bond tests results were used to indirectly calibrate an analytical approach based on mode-II fracture mechanics. A comparison between Cohesive Material Law (CML) functions at various temperatures was conducted for each of the three systems, demonstrating a good agreement between the analytical model and experimental curves. Furthermore, the durability in alkaline environment of two additional FRCM systems, characterized by basalt and glass fibre textiles with lime-based mortars, was studied through an extensive experimental campaign. Tests conducted on single yarn and textile specimens after exposure at different durations and temperatures revealed a significant impact on tensile capacity. Additionally, FRCM coupons manufactured with conditioned textile were tested to understand the influence of aged textile and curing environment on the final tensile behavior. These results contributed significantly to the existing knowledge on FRCM systems and could be used to develop a standardized alkaline testing protocol, still lacking in the scientific literature.